Project Description
Clear Online Low-E (70) China Manufacturer
BRAND: SSMG
GRADE:CLASS-A
COLOR: CLEAR
THICKNESS:3 MM-19 MM
FILM SYSTEM: ONLINE LOW-E 70
Clear Online Low-E (70) Size(mm):
| 1650*2140 | 1650*2250 | 1650*2440 |
| 1830*2140 | 1830*2250 | 1830*2440 |
| 3300*2140 | 3300*2250 | 3300*2440 |
| 3660*2140 | 3660*2250 | 3660*2440 |
| 5600*3300 | 11000*3300 | CUSTOM SIZE |
Description
SSM GLASS—CLEAR LOW-E GLASS(70) It adopts the world’s leading on-line coating technology, through high-temperature chemical vapor deposition (CVD) on the surface of high-quality ultra clear glass, annealed film and glass into one, with excellent chemical stability and mechanical stability, at the same time, the transmission and conductivity of the product reach a perfect balance. The on-line low-E energy-saving coated glass can meet the requirements of green buildings with high transmittance, low reflectivity, high thermal resistance and environmental protection and energy-saving. It can be widely used in civil residence, commercial curtain wall, electrical appliances, traffic locomotives and other fields.
Applications
The product has good chemical stability, strong and durable film, hot bending, toughening, and monolithic application. It is “hard coated” glass made by high temperature pyrolysis CVD method.
SSM GLASS—CLEAR LOW-E GLASS（70） can be used extensively in applications such as;
Advantages
Technology: adopt international advanced CVD on-line coating technology
Energy-saving: in winter, the film can reflect heat back to the building to prevent heat loss; in summer, reduce the secondary radiation into the room, reduce air conditioning and other energy consumption
Dura: the film is annealed and cooled into a part of glass, which is hard and durable.
Color: close to the color of glass itself
Storage and transportation: stable performance, long storage time, long life of membrane surface, and long-term exposure to air.
Processing: easy to clean, hollow, hot bending, tempering and gluing.
It can be used on a single chip.
Techonlogy
CLEAR LOW-E GLASS（70）-THERMOTECHNICAL AND OPTICS PERFORMANCE
| Single glass Coating in Pos.2 | Thickness | Visible Light | Solar energy | U-value | SHGC | SC | ||||
| （MM） | Trans | Reflectivity | Trans | Refle | Winter | Summer | ||||
| Nightime | daytime | |||||||||
| mittance | mittance | ctivity | W/m2K | W/m2K | ||||||
| Outside | Inside | |||||||||
| clear low-e glass | 4 | 83% | 9% | 11.00% | 72.00% | 12% | 3.7 | 2.8 | 0.75 | 0.86 |
| 5 | 83.50% | 10.00% | 11.50% | 71.50% | 12% | 3.7 | 2.9 | 0.74 | 0.85 | |
| 6 | 82.00% | 10.00% | 11.50% | 70.00% | 10% | 3.7 | 2.8 | 0.71 | 0.82 | |
| 8 | 82.00% | 10.00% | 11.00% | 69.00% | 9% | 3.7 | 2.9 | 0.73 | 0.84 | |
| 10 | 81.50% | 9.00% | 10.00% | 66.00% | 8% | 3.7 | 2.8 | 0.71 | 0.81 | |
Coated Glass